Nickel alloys refer to a broad range of heat and corrosion resistant materials where nickel constitutes over 40% of the composition. This guide provides an overview of various ニッケル合金粉 types, manufacturing methods, key applications, specifications, pricing, comparisons, and frequently asked questions for procurement.
Compositions of Nickel Alloy Powder
| 合金ファミリー | Major Alloying Elements | 共通グレード |
|---|---|---|
| 超合金 | Cr, Co, Mo, Ti, Al | インコネル718、625、ヘインズ282 |
| High temp alloys | Cr, Mo, W | Haynes 230, 188, HR-120 |
| 耐食性 | Cr, Mo | Alloy C-276, 20Cb-3, G-35-1 |
| Electrical / Electronic | Fe, Cu, Cr | Alloy 42, Kovar |
| Shape memory | Ti, Hf | Nitinol (NiTi) |
Various alloying elements like chromium, cobalt, iron, copper etc. added to tune mechanical properties, improve fabrication, and enhance corrosion and wear resistance.
Key Characteristics and Powder Properties
| 属性 | 代表値 |
|---|---|
| 粒子形状 | 球形 |
| サイズ範囲 | 10 – 150 microns |
| 酸素ppm | Below 500 ppm |
| ホール流量 | Around 25 secs for 50g |
| 見かけ密度 | 2 – 5 g/cc |
| 表面酸化物 | Thin passivated chromia film |
Particle characteristics tailored to suit production method – additive manufacturing needs spherical powders below 100 microns whereas cold spray better with larger particles.
Production Methods for Nickel Alloy Powder
| 方法 | 説明 |
|---|---|
| ガス噴霧 | Inert gas disintegrates molten metal into droplet powder |
| 水の霧化 | High pressure water breaks up melt stream |
| プラズマ霧化 | Very clean, small production volumes |
| カルボニルプロセス | Chemical precipitation from nickel carbonyl |
Gas atomization best suited for reactive alloys like superalloys, titanium etc. Water atomization more economical for high volumes above 30 microns. Plasma atomization and carbonyl route produce specialty powders.
の応用 ニッケル合金粉末
| 産業 | Common Components |
|---|---|
| 航空宇宙 | Turbine blades, discs, transitions |
| 石油・ガス | Wellhead equipment, valves, fasteners |
| 自動車 | Exhaust system parts, fuel cells |
| Chemical Process | 熱交換器、反応容器 |
| メディカル | Implants, surgical tools |
| アディティブ・マニュファクチャリング | Bi-metal parts, lattices, topology optimized designs |
Nickel alloys serve critical applications needing combination of high strength and corrosion resistance at elevated temperatures.
Specifications for Nickel Alloy Powder
| スタンダード | 説明 |
|---|---|
| ASTM B162 | Nickel plating grade specifications |
| ASTM B214 | Porous nickel strip |
| ASTM B351 | Wrought superalloy product forms |
| ASTM B777 | Powder metallurgy (PM) nickel alloys |
No universal powder specifications exist. Application and intended production method instead determines acceptance norms.
Nickel Alloy Powder Suppliers and Pricing
| Vendor | リードタイム | Price Range ($/kg) |
|---|---|---|
| サンドビック・オスプレイ | 10-16 weeks | $25 – $500 |
| アトランティック・エクイップメント | 12-18 weeks | $30 – $450 |
| TLSテクニーク | 16-20 weeks | $35 – $480 |
Pricing varies widely depending on alloy composition, powder quantity, size range and quality level specified.
の長所と短所 ニッケル合金粉末
| 長所 | 短所 |
|---|---|
| High strength at elevated temps | Expensive alloy raw materials |
| Withstand harsh environments | 限られたサプライヤーと入手可能性 |
| Custom alloys for tailored properties | Strict quality procedures to ensure purity |
| Flexible production methods | Safety hazards with fine metal powders |
| Complex shapes from AM technology | Post processing often essential after AM builds |
Nickel alloy powders enable fabrication of high performance components but require significant expertise to manufacture and handle safely.
よくあるご質問
What is the difference between superalloys, high temp alloys and stainless alloys?
Superalloys have highest strength thanks to gamma prime precipitate strengthening. High temp alloys beat oxidation. Stainless alloys focus on corrosion resistance.
What particle size range works best for binder jet printing?
Around 20 to 50 microns needed for binding process. Too fine powders inhibit liquid saturation and binder spread. Ensure narrow distribution for packing density.
What causes contamination during atomization?
Oxygen pickup from air leads to oxide inclusions. Minor element loss by vaporization possible. Other sources are tundish liners, melt crucibles. Use high purity inert gas and starting materials.
Why is gas atomized powder preferred over water atomized?
Water atomization leads to oxygen pickup degrading powder quality. Cooling rates slower leading to carbide networks which lower corrosion resistance. Avoid for reactive alloys.
What are common defects when printing nickel alloys?
Lack of fusion defects due to poor energy density. Residual stress cracking. Powder trapped inside enclosed volumes. Porosity from gas entrapment. Require integrated solution development.
結論
Nickel alloy powders provide extreme environments capability essential in critical applications, with customized compositions and particle properties available through specialized manufacturing processes. Careful specification and testing ensures suitability for production methods like additive manufacturing, thermal spray, or powder injection molding.